SHEETS – Alloy C 17200 CuBe2 DIN 2.1247

Melting point (°C): 865 – 980
Density: approx. 8.26 g/cm³

Sheet thickness <1 mm = hardness HV 180-210 – hardening 1/2H
Sheet thickness 1 – 6 mm = hardness HRC 5-15 – curing 1/2H
Tensile strength Rm (N/mm²): 700
Electrical conductivity: 18-24 (%IACS)

Sheet thickness 7 mm and > 7 mm = hardness HRC 36-40 – curing H
Tensile strength Rm (N/mm²): 1105
Electrical conductivity: 18-24 (%IACS)

Composition Weight:
Be: 1.8 – 2.0 %
Cu + rest: 99.5 % min.

Maximum width 200 mm – Maximum length 1000 mm
Surface machined to tolerance DIN ISO 2768 m.

Processing of the sheets by water jet cutting (contour cutting) according to customer specification or drawings is possible.